6082
EDOBO
6082 aluminum alloy is an alloy in the wrought aluminum magnesium silicon series (6000 or 6xxx series). It is one of the more popular alloys in its family (alongside alloys 6005, 6061 and 6063), although it is not prominently featured in ASTM (North American) standards. It is usually formed by extrusion and rolling, but as a wrought alloy, it is not used for casting. It can also be forged and clad, but this is not a common practice for this alloy. It cannot be work hardened, but is usually heat treated to produce a stronger but less ductile temper.
Aluminium Grade | 6082 |
Material Temper | F, O, H112, T4, T6, T651 |
Thickness (mm) | 0.2-500 |
Width (mm) | 20-2650 |
Length (mm) | Customized |
Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
6082 Alloy Sheet - T6 | 0.2 - 3.0 | 295 | 255 | 8 |
3.0 - 6.0 | 295 | 240 | 8 | |
6.0 - 25.00 | 295 | 240 | 8 |
6082 aluminum alloy is an alloy in the wrought aluminum magnesium silicon series (6000 or 6xxx series). It is one of the more popular alloys in its family (alongside alloys 6005, 6061 and 6063), although it is not prominently featured in ASTM (North American) standards. It is usually formed by extrusion and rolling, but as a wrought alloy, it is not used for casting. It can also be forged and clad, but this is not a common practice for this alloy. It cannot be work hardened, but is usually heat treated to produce a stronger but less ductile temper.
Aluminium Grade | 6082 |
Material Temper | F, O, H112, T4, T6, T651 |
Thickness (mm) | 0.2-500 |
Width (mm) | 20-2650 |
Length (mm) | Customized |
Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
6082 Alloy Sheet - T6 | 0.2 - 3.0 | 295 | 255 | 8 |
3.0 - 6.0 | 295 | 240 | 8 | |
6.0 - 25.00 | 295 | 240 | 8 |
Understanding the Differences Between 3003 and 5005 Aluminum Aluminum alloys are widely used in various industries due to their excellent properties, such as lightweight, corrosion resistance, and high strength. Among the numerous aluminum alloys available, 3003 and 5005 aluminum alloys are two of
Aluminum is a versatile material that is used in a wide range of industries, from aerospace to automotive to construction. One of the most popular aluminum alloys is 2024, which is known for its high strength and excellent machinability. Within the 2024 alloy family, two of the most common tempers a
6061-T6 temper: After xrlutian treatment, it is cooled to achieve high strength and no longer subjected to cold processing; 6061-T651 temper: After xrlutian treatment, it is cooled to achieve high strength, and then cold stretched by a stretching machine to eliminate residual internal stress after heat treatment, achieving no deformation after deep processing to ensure the precision of machined products.
The common states of 6061 aluminum plate include O state, T4 state, T6 state, and T651 state. The T651 state alloy is formed by stretching on the basis of T6 state to eliminate internal stress, making it more suitable for processing and forming.The difference between T6 and T651 states of 6061 alumi
China Photovoltaic Industry Briefing: From January to November, the installed photovoltaic capacity reached 163.8 kilowattsThe National Energy Administration of China stated that in the first 10 months of this year, China installed 163 gigawatts of solar energy, and by the end of November, the cumul