6082 aluminum sheet belongs to the 6××× series (Al-Mg-Si) alloy aluminum plate. It is an aluminum alloy plate that can be strengthened by heat treatment. It has medium strength, good welding performance, and corrosion resistance. It is mainly used for transportation, structural engineering industry and machining industry.
| Quantity: | |
|---|---|
Aluminium Grade | 6082 |
Material Temper | F, O, H112, T4, T6, T651 |
Thickness (mm) | 0.2-500 |
Width (mm) | 20-2650 |
Length (mm) | Customized |
Alloy | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
6082 | Rem. | 0.7-1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
6082 Alloy Sheet - T6
| 0.2 - 3.0 | 295 | 255 | 8 |
3.0 - 6.0 | 295 | 240 | 8 | |
6.0 - 25.00 | 295 | 240 | 8 |
1. Good formability, solderability and traceability.
2. It has medium strength and good machinability.
3. Good usability and excellent interface characteristics.
4. Easy to process, good anode reaction performance and easy coating.
5. Good corrosion resistance and oxidation resistance.
Aluminium Grade | 6082 |
Material Temper | F, O, H112, T4, T6, T651 |
Thickness (mm) | 0.2-500 |
Width (mm) | 20-2650 |
Length (mm) | Customized |
Alloy | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
6082 | Rem. | 0.7-1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
6082 Alloy Sheet - T6
| 0.2 - 3.0 | 295 | 255 | 8 |
3.0 - 6.0 | 295 | 240 | 8 | |
6.0 - 25.00 | 295 | 240 | 8 |
1. Good formability, solderability and traceability.
2. It has medium strength and good machinability.
3. Good usability and excellent interface characteristics.
4. Easy to process, good anode reaction performance and easy coating.
5. Good corrosion resistance and oxidation resistance.