5052 aluminum plate is AL-Mg series alloy aluminum plate. Magnesium is the main alloying element in 5052 alloy aluminum plate. It is the most widely used anti-rust aluminum. This alloy has high strength, especially fatigue resistance: plasticity and corrosion resistance. High performance, cannot be strengthened by heat treatment, good plasticity during semi-cold work hardening, low plasticity during cold work hardening, good corrosion resistance, good weldability, poor machinability, and can be polished.
Availability: | |
---|---|
Quantity: | |
5052
EDOBO
Chemical composition of 5052 aluminum plate
Al :reminder
Si: ≤0.25
Cu :≤0.10
Mg:2.2~2.8
Zn:≤0.10
Mn:≤0.10
Cr:0.15~0.35
Fe: ≤0.40
each:≤0.05;total:≤0.15
Performance of 5052 aluminum plate:
⑴Forming performance
①The alloy has good hot process plasticity. The forging and die forging temperature is 420~475°C, and the thermal deformation with a deformation rate of 80% is performed within this temperature range.
②The cold stamping performance is related to the alloy state. The cold stamping performance in the annealed (O) state is good, followed by the H32 and H34 state, and the H36/H38 state is not good.
⑵Welding performance
①The alloy has good performance in gas welding, arc welding, resistance welding, spot welding, and seam welding. Crystal cracks tend to appear during two argon arc welding. The brazing performance is still good, but the soft brazing performance is poor.
②The strength and plasticity of the weld are high, and the strength of the weld is 90%-95% of the strength of the base metal. However, the airtightness of the weld is not high. It is recommended to use 5A03 alloy as the solder, which can improve its airtightness and eliminate the tendency of cracks.
⑶Machining performance
The cutting performance of the alloy in the annealed state is not good, but it is improved in the cold hardened state.
The Specifications of 1100 Aluminium Plate
Thickness: 6 mm-200mm
Width: 200 mm-2250 mm
Length: Coil or as required
Temper: H14, H16, H18, H22, H24, O temper
Chemical composition of 5052 aluminum plate
Al :reminder
Si: ≤0.25
Cu :≤0.10
Mg:2.2~2.8
Zn:≤0.10
Mn:≤0.10
Cr:0.15~0.35
Fe: ≤0.40
each:≤0.05;total:≤0.15
Performance of 5052 aluminum plate:
⑴Forming performance
①The alloy has good hot process plasticity. The forging and die forging temperature is 420~475°C, and the thermal deformation with a deformation rate of 80% is performed within this temperature range.
②The cold stamping performance is related to the alloy state. The cold stamping performance in the annealed (O) state is good, followed by the H32 and H34 state, and the H36/H38 state is not good.
⑵Welding performance
①The alloy has good performance in gas welding, arc welding, resistance welding, spot welding, and seam welding. Crystal cracks tend to appear during two argon arc welding. The brazing performance is still good, but the soft brazing performance is poor.
②The strength and plasticity of the weld are high, and the strength of the weld is 90%-95% of the strength of the base metal. However, the airtightness of the weld is not high. It is recommended to use 5A03 alloy as the solder, which can improve its airtightness and eliminate the tendency of cracks.
⑶Machining performance
The cutting performance of the alloy in the annealed state is not good, but it is improved in the cold hardened state.
The Specifications of 1100 Aluminium Plate
Thickness: 6 mm-200mm
Width: 200 mm-2250 mm
Length: Coil or as required
Temper: H14, H16, H18, H22, H24, O temper
Understanding the Differences Between 3003 and 5005 Aluminum Aluminum alloys are widely used in various industries due to their excellent properties, such as lightweight, corrosion resistance, and high strength. Among the numerous aluminum alloys available, 3003 and 5005 aluminum alloys are two of
Aluminum is a versatile material that is used in a wide range of industries, from aerospace to automotive to construction. One of the most popular aluminum alloys is 2024, which is known for its high strength and excellent machinability. Within the 2024 alloy family, two of the most common tempers a
6061-T6 temper: After xrlutian treatment, it is cooled to achieve high strength and no longer subjected to cold processing; 6061-T651 temper: After xrlutian treatment, it is cooled to achieve high strength, and then cold stretched by a stretching machine to eliminate residual internal stress after heat treatment, achieving no deformation after deep processing to ensure the precision of machined products.
The common states of 6061 aluminum plate include O state, T4 state, T6 state, and T651 state. The T651 state alloy is formed by stretching on the basis of T6 state to eliminate internal stress, making it more suitable for processing and forming.The difference between T6 and T651 states of 6061 alumi